Photoluminescence in manganese indium sulphide thin films deposited by chemical spray pyrolysis

Title Photoluminescence in manganese indium sulphide thin films deposited by chemical spray pyrolysis
Author: Sharma, R K; Lakshmikumar, S T; Singh, Gurmeet & Rastogi, A C
Materials Chemistry and Physics, 2005
2005
http://www.sciencedirect.com/science/article/pii/S0254058405000313
More details: Photoluminescence measurements on manganese indium sulphide thin films were carried out and the temperature dependence of the Pl emission band was studied. A Gaussian shaped Pl band centered at 535\&\#xa0;nm was observed at 10\&\#xa0;K. A study on the variation of InCl3 concentration in spray solution over the Pl energy band position and shape suggests that varying InCl3 concentration in the solution or by changing the In3+ composition in the film during growth does not affect Pl maxima position on energy axis whereas a reduction in the Pl peak intensity was noticed with decreasing InCl3 solution concentration. Based on the luminescence data donor level height in the manganese indium sulphide energy gap was estimated and found to be around 20\&\#xa0;meV; that again on reduction in InCl3 concentration in solution found to decreases marginally. MnIn2S4,Photoluminescence,Spray deposition,Thin film

No comments:

Post a Comment